Vydyne® 41H

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne 41H is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 41H was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.

 

Vydyne 41H is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline.

 

Typical Applications/End Uses:

Vydyne 41H is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-100757495

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 冲击改性剂

• 冲击改性 • 可加工性，良好 • 耐化学性良好

特性 • 抗溶剂性 • 良好耐磨损性 • 耐汽油性

• 抗撞击性，高 • 耐低温冲击 • 耐油性能

• 齿轮 • 紧固件 • 消费品应用领域

用途 • 电气/电子应用领域 • 连接器

• 工业应用 • 汽车领域的应用

机构评级 • ASTM D 4066 PA0181 • ASTM D 6779 PA0181

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.08 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 2.00 mm 1.6 -- %

流动方向 : 2.00 mm 1.8 -- %

吸水率 ISO 62

23°C, 24 hr 1.0 -- %

平衡, 23°C, 50% RH 2.1 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 1860 1390 MPa ISO 527-2

拉伸应力 ISO 527-2

屈服, 23°C 50.0 35.0 MPa

断裂, 23°C 43.0 39.0 MPa

拉伸应变 (断裂, 23°C) 50 180 % ISO 527-2

弯曲模量 (23°C) 1750 545 MPa ISO 178

弯曲应力 (23°C) 53.0 17.0 MPa ISO 178

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179

-40°C 20 25 kJ/m²

-30°C 35 25 kJ/m²

23°C 76 110 kJ/m²

 

Vydyne® 41H

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁无缺口冲击强度 ISO 179

-30°C 无断裂 无断裂

23°C 无断裂 无断裂

悬壁梁缺口冲击强度 ISO 180

-40°C 22 25 kJ/m²

-30°C 40 29 kJ/m²

23°C 78 88 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 145 -- °C ISO 75-2/B

1.8 MPa, 未退火 58.0 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 1.7E-4 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.5E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 130 -- °C

1.50 mm 130 -- °C

3.00 mm 130 -- °C

RTI Imp UL 746

0.750 mm 75.0 -- °C

1.50 mm 75.0 -- °C

3.00 mm 75.0 -- °C

RTI UL 746

0.750 mm 115 -- °C

1.50 mm 120 -- °C

3.00 mm 125 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+10 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 14 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 6 -- ASTM D495

漏电起痕指数 (3.00 mm) 600 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 2 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 4 --

3.00 mm PLC 3 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 725 -- °C

1.50 mm 725 -- °C

3.00 mm 675 -- °C

 

 

Vydyne® 41H

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制   测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 750 -- °C

1.50 mm 750 -- °C

3.00 mm 700 -- °C

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

 